In this paper SrBi4Ti4O15 (SBTi), a perovskite-type ceramic, with cation
deficit A(5)B(4)O(15), was prepared by solid-state reaction method and
PbO and V2O5 were added into SBTi (2, 5, 10 and 15 wt%). Samples were
characterized through X-Ray Diffraction (XRD), Raman Spectroscopy and
Scanning Electron Microscopy (SEM). Impedance Spectroscopy was carried
out at room temperature. The analysis by XRD using the Rietveld
refinement has confirmed the formation of single-phase compound with a crystalline tetragonal system (a = 3.8408
%0 Journal Article
%1 WOS:000323249800048
%A Jr., C A Rodrigues
%A Filho, J M S
%A Silva, P M O
%A Silva, M A S
%A Junqueira, C C M
%A Sombra, A S B
%C VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS
%D 2013
%I SPRINGER
%J JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
%K imported
%N 9
%P 3467-3473
%R 10.1007/s10854-013-1271-6
%T High dielectric permittivity and low loss of SrBi4Ti4O15 with PbO and
V2O5 additions for RF and microwave applications
%V 24
%X In this paper SrBi4Ti4O15 (SBTi), a perovskite-type ceramic, with cation
deficit A(5)B(4)O(15), was prepared by solid-state reaction method and
PbO and V2O5 were added into SBTi (2, 5, 10 and 15 wt%). Samples were
characterized through X-Ray Diffraction (XRD), Raman Spectroscopy and
Scanning Electron Microscopy (SEM). Impedance Spectroscopy was carried
out at room temperature. The analysis by XRD using the Rietveld
refinement has confirmed the formation of single-phase compound with a crystalline tetragonal system (a = 3.8408
@article{WOS:000323249800048,
abstract = {In this paper SrBi4Ti4O15 (SBTi), a perovskite-type ceramic, with cation
deficit A(5)B(4)O(15), was prepared by solid-state reaction method and
PbO and V2O5 were added into SBTi (2, 5, 10 and 15 wt%). Samples were
characterized through X-Ray Diffraction (XRD), Raman Spectroscopy and
Scanning Electron Microscopy (SEM). Impedance Spectroscopy was carried
out at room temperature. The analysis by XRD using the Rietveld
refinement has confirmed the formation of single-phase compound with a crystalline tetragonal system (a = 3.8408},
added-at = {2022-05-23T20:00:14.000+0200},
address = {VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS},
author = {Jr., C A Rodrigues and Filho, J M S and Silva, P M O and Silva, M A S and Junqueira, C C M and Sombra, A S B},
biburl = {https://www.bibsonomy.org/bibtex/27921dfb459d4e2c460695b66629d7836/ppgfis_ufc_br},
doi = {10.1007/s10854-013-1271-6},
interhash = {c68eefdd11367f79847ce05d672a9dce},
intrahash = {7921dfb459d4e2c460695b66629d7836},
issn = {0957-4522},
journal = {JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS},
keywords = {imported},
number = 9,
pages = {3467-3473},
publisher = {SPRINGER},
pubstate = {published},
timestamp = {2022-05-23T20:00:14.000+0200},
title = {High dielectric permittivity and low loss of SrBi4Ti4O15 with PbO and
V2O5 additions for RF and microwave applications},
tppubtype = {article},
volume = 24,
year = 2013
}