Synthesis and Characterization of Cesium Salt of 12-Tungstophosphoric Acid Supported on SBA-15
E. Akbay, and G. Demir. International Journal of Innovative Science and Modern Engineering (IJISME), 5 (1):
7-9(November 2017)
Abstract
12-tungstophosporic acid of cesium salt supported on SBA-15 (Cs-TPA/SBA-15) was synthesized by the two-step impregnation technique. Acidic cesium salts supported on SBA-15 at 20%, 40% and 60% loading were synthesized and characterized. Then obtained catalyst have been characterized by XRD, FT-IR, FT-IR spectroscopy of pyridine adsorption, BET analysis, SEM and XRF. It was seen that Cs-TPA was hold on to SBA-15. At high loading percentage, structure of SBA-15 has been deformed.
%0 Journal Article
%1 noauthororeditor
%A Akbay, Elif
%A Demir, Gülberk
%D 2017
%E Kumar, Dr. Shiv
%J International Journal of Innovative Science and Modern Engineering (IJISME)
%K 12-Tungstophosporic Acid Cesium SBA-15. Salt
%N 1
%P 7-9
%T Synthesis and Characterization of Cesium Salt of 12-Tungstophosphoric Acid Supported on SBA-15
%U https://www.ijisme.org/wp-content/uploads/papers/v5i1/A1057085117.pdf
%V 5
%X 12-tungstophosporic acid of cesium salt supported on SBA-15 (Cs-TPA/SBA-15) was synthesized by the two-step impregnation technique. Acidic cesium salts supported on SBA-15 at 20%, 40% and 60% loading were synthesized and characterized. Then obtained catalyst have been characterized by XRD, FT-IR, FT-IR spectroscopy of pyridine adsorption, BET analysis, SEM and XRF. It was seen that Cs-TPA was hold on to SBA-15. At high loading percentage, structure of SBA-15 has been deformed.
@article{noauthororeditor,
abstract = {12-tungstophosporic acid of cesium salt supported on SBA-15 (Cs-TPA/SBA-15) was synthesized by the two-step impregnation technique. Acidic cesium salts supported on SBA-15 at 20%, 40% and 60% loading were synthesized and characterized. Then obtained catalyst have been characterized by XRD, FT-IR, FT-IR spectroscopy of pyridine adsorption, BET analysis, SEM and XRF. It was seen that Cs-TPA was hold on to SBA-15. At high loading percentage, structure of SBA-15 has been deformed.},
added-at = {2021-09-17T13:36:23.000+0200},
author = {Akbay, Elif and Demir, Gülberk},
biburl = {https://www.bibsonomy.org/bibtex/2e1c386cc78f980c7a3e9f4e7d2a90e62/ijisme_beiesp},
editor = {Kumar, Dr. Shiv},
interhash = {754764e90ceb44498aa0e892b5518b83},
intrahash = {e1c386cc78f980c7a3e9f4e7d2a90e62},
issn = {2319-6386},
journal = {International Journal of Innovative Science and Modern Engineering (IJISME)},
keywords = {12-Tungstophosporic Acid Cesium SBA-15. Salt},
language = {En},
month = {November},
number = 1,
pages = {7-9},
timestamp = {2021-09-17T13:36:23.000+0200},
title = {Synthesis and Characterization of Cesium Salt of 12-Tungstophosphoric Acid Supported on SBA-15},
url = {https://www.ijisme.org/wp-content/uploads/papers/v5i1/A1057085117.pdf},
volume = 5,
year = 2017
}