The microstructure of alkali-etched heated kaolinitic-illitic clay, which was cured in wet atmosphere at different temperatures and times, was investigated by using X-ray diffraction, Fourier-transform infrared spectroscopy, thermal analysis and scanning electron microscope. The flexural strength, density and water absorption of the cured samples were correlated to curing time, ageing temperature and alkaline solution concentration by using the response surface methodology. It was found that hydro-sodalite and zeolite P were essentially formed from metakaolinite, the products of chlorite and illite. The geopolymer was almost absent mainly because of excessive hydration. The assemblage of neoformed zeolites differed partially from that predicted using the stability diagram Na2O–SiO2–Al2O3. Polynomial models described well the change of the physical/mechanical properties against the experimental factors. Based on the results of the models, the increase of any factor among the studied ones had an adverse effect on the mechanical strength and contributed to the increase of water absorption. The weight of the effect of the factors on density was less significant. These results were discussed in relation to the microstructure investigation.
%0 Journal Article
%1 El_Hafid_2016
%A El Hafid, Kenza
%A Hajjaji, Mohamed
%D 2016
%I Informa UK Limited
%J Journal of Asian Ceramic Societies
%K Activation Alkaline Clays Deconvolution Geopolymers Mechanical Microstructure RSM methodology physical properties
%N 3
%P 234--242
%R 10.1016/j.jascer.2016.07.001
%T Alkali-etched heated clay: Microstructure and physical/mechanical properties
%U https://doi.org/10.1016%2Fj.jascer.2016.07.001
%V 4
%X The microstructure of alkali-etched heated kaolinitic-illitic clay, which was cured in wet atmosphere at different temperatures and times, was investigated by using X-ray diffraction, Fourier-transform infrared spectroscopy, thermal analysis and scanning electron microscope. The flexural strength, density and water absorption of the cured samples were correlated to curing time, ageing temperature and alkaline solution concentration by using the response surface methodology. It was found that hydro-sodalite and zeolite P were essentially formed from metakaolinite, the products of chlorite and illite. The geopolymer was almost absent mainly because of excessive hydration. The assemblage of neoformed zeolites differed partially from that predicted using the stability diagram Na2O–SiO2–Al2O3. Polynomial models described well the change of the physical/mechanical properties against the experimental factors. Based on the results of the models, the increase of any factor among the studied ones had an adverse effect on the mechanical strength and contributed to the increase of water absorption. The weight of the effect of the factors on density was less significant. These results were discussed in relation to the microstructure investigation.
@article{El_Hafid_2016,
abstract = {The microstructure of alkali-etched heated kaolinitic-illitic clay, which was cured in wet atmosphere at different temperatures and times, was investigated by using X-ray diffraction, Fourier-transform infrared spectroscopy, thermal analysis and scanning electron microscope. The flexural strength, density and water absorption of the cured samples were correlated to curing time, ageing temperature and alkaline solution concentration by using the response surface methodology. It was found that hydro-sodalite and zeolite P were essentially formed from metakaolinite, the products of chlorite and illite. The geopolymer was almost absent mainly because of excessive hydration. The assemblage of neoformed zeolites differed partially from that predicted using the stability diagram Na2O–SiO2–Al2O3. Polynomial models described well the change of the physical/mechanical properties against the experimental factors. Based on the results of the models, the increase of any factor among the studied ones had an adverse effect on the mechanical strength and contributed to the increase of water absorption. The weight of the effect of the factors on density was less significant. These results were discussed in relation to the microstructure investigation.},
added-at = {2019-10-14T01:19:34.000+0200},
author = {El Hafid, Kenza and Hajjaji, Mohamed},
biburl = {https://www.bibsonomy.org/bibtex/2a1a9a1991621e62cb96ddb5a0c59c0ea/kutuqueen},
description = {The paper is freely available on Sciendirect.},
doi = {10.1016/j.jascer.2016.07.001},
interhash = {797663bb9863f9afe2526b3a169292f8},
intrahash = {a1a9a1991621e62cb96ddb5a0c59c0ea},
journal = {Journal of Asian Ceramic Societies},
keywords = {Activation Alkaline Clays Deconvolution Geopolymers Mechanical Microstructure RSM methodology physical properties},
language = {English},
month = sep,
number = 3,
pages = {234--242},
publisher = {Informa {UK} Limited},
timestamp = {2019-10-16T00:28:12.000+0200},
title = {Alkali-etched heated clay: Microstructure and physical/mechanical properties},
url = {https://doi.org/10.1016%2Fj.jascer.2016.07.001},
volume = 4,
year = 2016
}